Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel

Gülcan Toktaş [1] , Alaaddin Toktaş [2] , Murat Can Duran [3]

315 431


100Cr6 steel surface was induction hardened in order to be used in a bushing manufacturing.  After examininig the microstructure and hardness variations of the hardened surfaces, ball-on disc type wear tests were carried out.  Wear tests were performed at 4,92 mm/s sliding speed, under various loads (2,5-5-10 N), in dry medium and at room temperature.  The results of wear tests were evaluated by the mass loss method.  The coefficients of friction were obtained during wear tests.   The wear tracks and surfaces were investigated by optic and scanning electron microscopes. 

As a result, the surface hardness of the steel was obtained 2,5 times more than the core hardness by the aid of formed martensitic matrix structure instead of pearlitic one on steel surface by induction hardening process. It is seen that the highest mass loss was obtained by applying 5 N load in wear tests.

100Cr6 Steel, Induction Hardening, Wear
  • [1] M. C. M. J. Schneider, "Introduction to surface hardening of steel," in ASM Handbook, Heat Treating, ASM International, vol. 4A, J. Dossett, Ed. 1991, pp. 259-267.
  • [2] E.C. Santos, K. Kida, T. Honda, H. Koike a. J. Rozwadowska, "Fatigue strength improvement of AISI 52100 bearing steel by induction and repeated quenching," Mater. Sci., vol.47, no.5, pp. 677-682, Mar 2012.
  • [3] J. Grum, Induction heat treating, Encyclopedia of tribology, Springer, pp.1796-1808, 2013.
  • [4] P. V. Krishna,R. R. Srikant, M. Iqbal, N. Sriram, "Effect of austempering and martempering on the properties of AISI 52100 steel," ISRN Tribology, vol. 2013, Article ID 515484, 6 pages, 2013.
  • [5] V. Rudnev, G.A. Fett A. Griebel, J. Tartaglia, Principles of induction hardening and inspection, ASM Handbook, vol.4c, ASM International.
  • [6] J. Yi, M. Gharghouri, P. Bocher, M. Medraj, "Distorsion and residual stress measurements of induction hardened AISI discs," Mater. Chem. Phys.,vol. 142, no. 1, pp. 248-258, oct 2013.
  • [7] G. V. B. Lemos, T. K.Hirsch, A. S. Rocha, R.M. Nunes, "Residual stressa analysis of drive shafts after induction hardening," Mater. Res., vol. 17, no.1, pp. 70-74, Apr 2014.
  • [8] M. Sharma, J. S. Kohli, S. Akhai, "Metallurgical analysis of cracks encountered during induction hardening of crankshafts," Int. J. Res. Adv. Tech., vol.2,no. 4, pp. 295-304, Apr 2014.
  • [9] A. Kusmoko, D. Dunne, R. Dahar, H. Li, "Surface treatment evaluation of induction hardened and tempered 1045 steel," Int. j. curr.eng. tech., pp. 1236-1239, june 2014.
  • [10] K. Sipos, M. Lopez, M. Trucco, "Surface martensite white layer produced by adhesive sliding wear-friction in AISI 1065 steel," Revista Latinoamerica de Metalurgia Materiales, vol.28, no.1, pp. 46-50, june 2008.
Birincil Dil en
Konular Malzeme Bilimi
Yayımlanma Tarihi October 2018
Dergi Bölümü Araştırma Makalesi
Yazarlar

Yazar: Gülcan Toktaş
Kurum: BALIKESİR ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, MAKİNE MÜHENDİSLİĞİ BÖLÜMÜ
Ülke: Turkey


Yazar: Alaaddin Toktaş
Kurum: BALIKESİR ÜNİVERSİTESİ, MÜHENDİSLİK FAKÜLTESİ, MAKİNE MÜHENDİSLİĞİ BÖLÜMÜ
Ülke: Turkey


Yazar: Murat Can Duran
Kurum: Balıkesir Büyükşehir Belediyesi
Ülke: Turkey


Bibtex @araştırma makalesi { saufenbilder304203, journal = {Sakarya University Journal of Science}, issn = {1301-4048}, eissn = {2147-835X}, address = {Sakarya Üniversitesi}, year = {2018}, volume = {22}, pages = {1174 - 1180}, doi = {10.16984/saufenbilder.304203}, title = {Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel}, key = {cite}, author = {Duran, Murat Can and Toktaş, Gülcan and Toktaş, Alaaddin} }
APA Toktaş, G , Toktaş, A , Duran, M . (2018). Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel. Sakarya University Journal of Science, 22 (5), 1174-1180. DOI: 10.16984/saufenbilder.304203
MLA Toktaş, G , Toktaş, A , Duran, M . "Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel". Sakarya University Journal of Science 22 (2018): 1174-1180 <http://www.saujs.sakarya.edu.tr/issue/31265/304203>
Chicago Toktaş, G , Toktaş, A , Duran, M . "Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel". Sakarya University Journal of Science 22 (2018): 1174-1180
RIS TY - JOUR T1 - Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel AU - Gülcan Toktaş , Alaaddin Toktaş , Murat Can Duran Y1 - 2018 PY - 2018 N1 - doi: 10.16984/saufenbilder.304203 DO - 10.16984/saufenbilder.304203 T2 - Sakarya University Journal of Science JF - Journal JO - JOR SP - 1174 EP - 1180 VL - 22 IS - 5 SN - 1301-4048-2147-835X M3 - doi: 10.16984/saufenbilder.304203 UR - http://dx.doi.org/10.16984/saufenbilder.304203 Y2 - 2017 ER -
EndNote %0 Sakarya University Journal of Science Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel %A Gülcan Toktaş , Alaaddin Toktaş , Murat Can Duran %T Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel %D 2018 %J Sakarya University Journal of Science %P 1301-4048-2147-835X %V 22 %N 5 %R doi: 10.16984/saufenbilder.304203 %U 10.16984/saufenbilder.304203
ISNAD Toktaş, Gülcan , Toktaş, Alaaddin , Duran, Murat Can . "Investigating the Wear Behaviour of Induction Hardened 100Cr6 Steel". Sakarya University Journal of Science 22 / 5 (Ekim 2018): 1174-1180. http://dx.doi.org/10.16984/saufenbilder.304203