Yıl 2018, Cilt 22, Sayı 2, Sayfalar 417 - 426 2018-04-01

Effect of shrinkage reducing admixture on compressive strength, water absorption and drying-shrinkage of mortar mixture in the presence of water reducing admixture
Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi

Ali Mardani-Aghabaglou [1] , Metin İlhan [2]

159 234

In this study, compressive strength, water absorption and drying-shrinkage behaviour of shrinkage-reducing admixture (SRA) bearing mortar mixture were investigated. For this purpose, 9 powder and liquid commercial SRA admixtures provided from 4 different factories were used. In all mortar mixture, CEM I 42.5 R type cement as binder and standard sand as aggregate were used. In addition to the containing no SRA admixture, 10 different mortar mixtures were produced by using SRA admixture as 2 wt.% of the cement. In all mortar mixtures, water/cement ratio, sand/binder ratio and flow value were kept constant as 0.485, 2.75 and 230 ± 20 mm, respectively. A type of polycarboxylate-ether based high range water reducing admixture was used for providing the desired flow values. 1, 3, 7 and 28-day compressive strength and 28-day water absorption of mortar mixtures were obtained. Also, the 28-day drying-shrinkage of mortar mixtures was measured.

Test results demonstrated that utilization of SRA positively affected compressive strength and permeability of the mortar mixtures. However, utilization of SRA led to incompletion of setting time of mortar mixtures. In the mentioned mortar mixtures, water reducing admixture was not used. In addition, a reduction of %10-%45 was found in drying shrinkage value of mortar mixtures by utilization of SRA. The liquid types of SRA generally were more successful compared to the powder types in term of drying-shrinkage behaviour of mortar mixtures.

 Bu çalışmada, kuruma büzülme engelleyici (KBE) katkı içeren harç karışımlarının basınç dayanımı, su emme oranı ve kuruma büzülmesi incelenmiştir. Bu amaçla,4 farklı fabrika ürünü 9 adet toz ve sıvı halinde katkı kullanılmıştır. Tüm harç karışımlarında bağlayıcı olarak CEMI 42.5 R tipi çimento ve agrega olarak standart kum kullanılmıştır. KBE katkı içermeyen kontrol karışımına ilaveten çimento ağırlığının %2'si kadar KBE katkı kullanılarak toplamda 10 seri karışım hazırlanmıştır. Üretilen tüm harç karışımlarında, kum/bağlayıcı oranı, su/çimento (S/Ç) oranı ve yayılma değeri sırasıyla, 2.75, 0.485 ve 230±20 mm olarak sabit tutulmuştur. Hedeflenen yayılma değerlerini sağlamak için tek tip polikarboksilat-eter esaslı yüksek oranda su azaltıcı katkı kullanılmıştır. Hazırlanan harç karışımlarının 1, 3, 7 ve 28 günlük basınç dayanımları ve 28 günlük su emme oranı elde edilmiştir. Ayrıca söz konusu karışımların 28 günlük kuruma büzülme davranışı incelenmiştir.

Deney sonuçlarına göre, kontrol karışımına kıyasla, KBE katkı kullanımı ile harç karışımlarının basınç dayanımı ve geçirgenlik özellikleri genel olarak olumlu etkilenmiştir. Ancak, 2 farklı KBE katkı kullanımı harç karışımlarının priz almamasına sebep olmuştur. Söz konusu karışımlarda su azaltıcı katkı kullanılmamıştır. Ayrıca, KBE katkı kullanımı ile harç karışımlarının kuruma büzülme değerlerinde %10-%45 oranında azalmalar tespit edilmiştir. Sıvı halinde olan KBE katkılar genel olarak toz halinde olan katkılara kıyasla kuruma-büzülme davranışı açısından daha başarılı olmuştur.
  • [1] D.P., Bentz, M.R., Geiker, K.K., Hansen, “Shrinkage-Reducing Admixtures and Early-Age Desiccation in Cement Pastes and Mortars”, Cement and Concrete Research, No. 31, pp. 1075-1085, 2001.
  • [2] B. Baradan, H. Yazıcı ve H. Ün, Beton ve Betonarme Yapılarda Kalıcılık, 1st ed. Türkiye Hazır Beton Birliği, 2010.
  • [3] P.K., Mehta, P.J.M., Monteiro “Concrete: Microstructure, Properties and Materials”, 3th ed., McGraw-Hill, 2006.
  • [4] J., Saliba, E., Roziere, F., Grondin, A., Loukili, “Influence of Shrinkage-Reducing Admixtures on Plastic and Long-Term Shrinkage”, Cement and Concrete Composites, No. 33, pp. 209-217, 2011.
  • [5] K. J. Folliard and N. S. Berke, “Properties of high-performance concrete containing shrinkage-reducing admixture,” Cement and Concrete Research, vol. 27, no. 9, pp. 1357–1364, 1997.
  • [6] T. Kadıoğlu, "Rötre Azaltıcı Katkı Maddeleri", Yüksek Lisans Tezi, İstanbul Teknik Üniversitesi Fen Bilimleri Enstitüsü, 2006.
  • [7] F., Rajabipour, G., Sant, J., Weiss, “Interactions Between Shrinkage Reducing Admixtures (SRA) and Cement Paste's Pore Solution”, Cement and Concrete Research, No. 38, pp. 606-615, 2008.
  • [8] R., Bloom, and A., Bentur, 1992, Free and restrained shrinkage of normal and high strength concretes, ACI MaterialsJournal, 92, 211-217.
  • [9] M., Lopez, L.F., Kahn, K.E., Kurtis, 2004, Creep and shrinkage of high-performance lightweight concrete, ACI Materials Journal, 101, 391-399.
  • [10] J.M., Ruacho, R., Gettu, A., Aguado, “Influence of Shrinkage-Reducing Admixtures on the Reduction of Plastic Shrinkage Cracking in Concrete”, Cement and Concrete Research, No. 39, pp. 141-146, 2009.
  • [11] B., Rongbing, and S., Jian, “Synthesis and Evaluation of Shrinkage-Reducing Admixture for Cementitious Materials”, Cement and Concrete Research, No. 35, pp.445-448, 2005.
  • [12] N., Quangphu, J., Linhua, L., Jiaping, T., Qian, D., Tienquan, “Influence of Shrinkage-Reducing Admixture on Drying Shrinkage and mechanical Properties of High-Performance Concrete”, Water Science and Engineering, No. 1, pp. 67-74, 2008.
  • [13] M-H., Zhang, L., Li, P., Paramasivam, 2005, “Shrinkage of high-strength lightweight aggregate concrete exposed to dry environment”, ACI MaterialsJournal, 102, 86- 92.
  • [14] J.Y., Wang, N., Banthia, M.H., Zhang, “Effect of Shrinkage Reducing Admixture on Flexural Behaviors of Fiber Reinforced Cementitious Composites”, Cement and Concrete Composites, No. 34, pp. 443-450, 2012.
  • [15] D.Y., Yoo, A.T., Kang, J.H., Lee, Y.S., Yoon, “Effect of Shrinkage Reducing Admixture on Tensile and Flexural Behaviors of UHPFRC Considering Fiber Distribution Characteristics”, Cement and Concrete Research, No. 54, pp. 180-190, 2013.
  • [16] R., Gagne, Science and Technology of Concrete Admixtures, Chapter 22, 2016.
  • [17] A., Mardani, E., Yoğurtçu, Ö., Andiç, “WaterTransport of Lightweight Concrete with Different Aggregate Saturation Levels”, ACI MaterialsJournal, 112, 681-692.
  • [18] P.C., Aïtcin, High Performance Concrete, E&FN SPON, New York, 2004.
  • [19] TS EN 197-1, Genel Çimentolar-Bölüm 1: Genel Çimentolar- Bileşim, Özellikler ve Uygunluk Kriterleri, TSE, Ankara, 2012.
  • [20] TS EN 1097-6, Agregaların Mekanik ve Fiziksel Özellikleri İçin Deneyler - Bölüm 6: Tane Yoğunluğunun Ve Su Emme Oranının Tayini, TSE, Ankara, 2013.
  • [21] TS EN 196-1, Çimento deney metotları- Bölüm 1: Dayanım tayini, TSE, Ankara, 2016.
  • [21] TS EN 196-1, Çimento deney metotları - Bölüm 1: Dayanım tayini, TSE, Ankara, 2016.
  • [22] ASTM C109-16, Standard Test Method for Compressive Strength of Hydraulic Cement Mortars, ASTM International, West Conshohocken, PA, 2017.
  • [23] C1437-15, Standard Test Method for Flow of Hydraulic Cement Mortar, ASTM International, West Conshohocken, PA, 2017.
  • [24] ASTM C642-97, Standard Test Method for Density, Absorption, and Voids in Hardened Concrete, , ASTM International, West Conshohocken, PA, 2017.
  • [25] ASTM C596-01, Standard Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement, , ASTM International, West Conshohocken, PA, 2017.
Birincil Dil tr
Konular İnşaat Mühendisliği
Yayımlanma Tarihi Nisan 2018
Dergi Bölümü Araştırma Makalesi
Yazarlar

Yazar: Ali Mardani-Aghabaglou
Kurum: Uludağ Üniversitesi
Ülke: Turkey


Yazar: Metin İlhan
Ülke: Turkey


Bibtex @araştırma makalesi { saufenbilder342519, journal = {Sakarya University Journal of Science}, issn = {1301-4048}, eissn = {2147-835X}, address = {Sakarya Üniversitesi}, year = {2018}, volume = {22}, pages = {417 - 426}, doi = {10.16984/saufenbilder.342519}, title = {Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi}, key = {cite}, author = {İlhan, Metin and Mardani-Aghabaglou, Ali} }
APA Mardani-Aghabaglou, A , İlhan, M . (2018). Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi. Sakarya University Journal of Science, 22 (2), 417-426. DOI: 10.16984/saufenbilder.342519
MLA Mardani-Aghabaglou, A , İlhan, M . "Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi". Sakarya University Journal of Science 22 (2018): 417-426 <http://www.saujs.sakarya.edu.tr/issue/30829/342519>
Chicago Mardani-Aghabaglou, A , İlhan, M . "Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi". Sakarya University Journal of Science 22 (2018): 417-426
RIS TY - JOUR T1 - Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi AU - Ali Mardani-Aghabaglou , Metin İlhan Y1 - 2018 PY - 2018 N1 - doi: 10.16984/saufenbilder.342519 DO - 10.16984/saufenbilder.342519 T2 - Sakarya University Journal of Science JF - Journal JO - JOR SP - 417 EP - 426 VL - 22 IS - 2 SN - 1301-4048-2147-835X M3 - doi: 10.16984/saufenbilder.342519 UR - http://dx.doi.org/10.16984/saufenbilder.342519 Y2 - 2017 ER -
EndNote %0 Sakarya University Journal of Science Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi %A Ali Mardani-Aghabaglou , Metin İlhan %T Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi %D 2018 %J Sakarya University Journal of Science %P 1301-4048-2147-835X %V 22 %N 2 %R doi: 10.16984/saufenbilder.342519 %U 10.16984/saufenbilder.342519
ISNAD Mardani-Aghabaglou, Ali , İlhan, Metin . "Büzülme engelleyici katkıların su azaltıcı katkı varlığında harç karışımlarının basınç dayanımına, su emmesine ve kuruma-büzülmesine etkisi". Sakarya University Journal of Science 22 / 2 (Nisan 2018): 417-426. http://dx.doi.org/10.16984/saufenbilder.342519